The sessile drop method was used to study the interaction of liquid slag CaO-Al2O3-SiO2-MgO with the Al2O3-based refractory material. A decrease in the wetting angle to 15° in the initial 10 min of the experiment and the reduction to 6° for the next 110 min were found. The microstructure and elemental mapping of cross sections of the slag and ceramics were examined. The phase corresponding to CaAl12O19 at the grain boundaries of aluminum oxide in the refractory ceramics was formed. Its fraction in the initial ceramics was about 9% mass., whereas after experiment it was close to 25% mass. This indicates a chemical interaction of slag with the ceramics. In the central zone of interaction, a slag penetration into the ceramics was observed.
Метод лежащей капли использован для исследования взаимодействия жидкого шлака системы CaO-Al2O3-SiO2-MgO с огнеупорным материалом на базе Al2O3. Показано снижение значений краевого угла смачивания до 15° в первые 10 мин опыта и последующее уменьшение его значений до 6° в течение 110 мин. Исследована микроструктура и проведено элементов картирование границ поперечных орезов шлака и керамики. На границах зерен оксида алюминия в огнеупорном материале обнаружено образование фазы, соответствующей соединению CaAl12O19. Его доля в исходной керамике составила ~9 мас.%, в то время как в керамике после опыта ~25 мас.%, что указывает на химическое взаимодействие шлака с огнеупором. Зафиксировано проникновение шлака в глубь керамической подложки в центральной области взаимодействия.