Samples of Al-Ce-Fe-Ni-Zr alloy were obtained by selective laser melting at scanning speeds of 700–1900 mm/s. The structure of the samples is eutectic: a solid solution based on aluminum is located inside intermetallic cells. A coarser eutectic structure with coarser cells is observed at the cell boundary. The microhardness of the samples was HV0,1 = 115–170, the tensile strength was 370–475 MPa, and the ductility was 10–23%. Residual thermal stresses <250 MPa were observed in the samples. An increase in energy density contributed to a decrease in strength characteristics, an increase in elongation, and a decrease in residual stress.
Селективным лазерным плавлением получены образцы сплава Al-Ce-Fe-Ni-Zr при скоростях сканирования 700–1900 мм/с. Структура образцов – эвтектическая (твердый раствор на основе алюминия находится внутри интерметаллидных ячеек). На границе ячеек наблюдается более грубая эвтектическая структура с ячейками большего размера. Микротвердость образцов составила HV0,1 115–170, предел прочности 370–475 МПа, пластичность 10–23%. В образцах наблюдаются остаточные термические напряжения <250 МПа. Увеличение плотности энергии способствовало снижению прочностных характеристик, увеличению пластичности сплава, а также уменьшению остаточных макропапряжений.